Fabrication and Characterization of a Multifunctional Coating to Promote the Osteogenic Properties of Orthopedic Implants

Abstract

Titanium-based alloys are used in orthopedic applications as fixation elements, hard tissue replacements in artificial bones, and dental implants. Despite their wide range of applications, metallic implant defects and failures arise due to inadequate mechanical bonding, postoperative clotting problems, aseptic loosening, and infections. To improve the surface bioactivity and reduce the corrosion rate of the Ti6Al4V alloy, multi-layered coatings (HAp, BG, Cs, and Hep) were applied via electrophoretic deposition (EPD). XRD images showed the presence of HAp within the coating. In vitro investigation: cell line NIH-3T3 fibroblasts were seeded on the non-coated and coated Ti6Al4V substrates, and their cellular behavior was evaluated. The results indicated that the HApBGCsHep coating could enhance the adhesion and proliferation of NIH 3T3 cells. In addition, the potentiodynamic polarization results are compatible with the in vitro outcome.