IImpact of uv irradiance on selected parameters of scots pine impregnated with some commonly used fire- retardants
Özet
This study was designed to determine some selected parameters such as gloss, surface roughness, and color changes of Scots pine wood impregnated with commonly used fire-retardant (FR) chemicals after UV irradiance. Sodium acetate (SA), ammonium chlorite (AC), zinc chlorite (ZC), ammoniumsulphate (AS), and di ammonium phosphate (DAP) were used as fire retardants. Wood specimens were prepared from Scots pine (Pinus sylvestris L.). Before test, wood specimens were impregnated with 5 % aqueous solution of chemicals according to ASTM D 1413-76 standard. Results showed that UV irradiance caused gloss loss and increase surface roughness of FR impregnated and un-treated (control) Scots pine specimen. DAP was the most effective chemical in terms of reducing gloss loss and surface roughness of Scots pine after 750 h UV irradiance exposure. UV irradiance caused a dark, reddish, and yellowish color of impregnated and un-treated (control) Scots pine specimen after all UV irradiance periods. Total color changes in color (Delta E*) exhibited a systematic trend to higher values with increasing UV irradiance time. Total color changes of ZC impregnated Scots pine were the lowest after 750 h UV irradiance exposure.